The present invention describes the use of porous metal oxides for the
preparative purification of antibodies and biomolecules within a range of
particle physical characteristics. Typically, particles from 15 to 100
microns in average diameter with pores sizes ranging from 400 to 600
angstroms and surface areas from 10 to 50 square meters per gram, and pore
volumes from 0.1 to 0.4 mL/gram can be used for purification processes.
The metal oxide particles that fall within this range of physical
properties show enhanced utility and greater chromatographic capacity for
antibodies than materials oxide particles falling outside of this range.
Metal oxides such as zirconia, titania and alumina can all be modified
with a multi-Lewis base moiety such as an organophosphate
ethylenediamine-N,N-tetra(methylenephosphonic) acid (EDTPA), to produce a
bio-compatible purification media for, biomolecules.
De onderhavige uitvinding beschrijft het gebruik van poreuze metaaloxyden voor de voorbereidende reiniging van antilichamen en biomoleculen binnen een waaier van deeltjes fysieke kenmerken. Typisch, kunnen de deeltjes van 15 tot 100 microns in gemiddelde diameter met poriëngrootte die zich van 400 tot 600 angstroms en oppervlakten van 10 tot 50 vierkante meters per gram uitstrekken, en de porievolumes van 0,1 tot 0,4 mL/het gram voor reinigingsprocessen worden gebruikt. De deeltjes van het metaaloxyde die binnen dit gamma van fysieke eigenschappen vallen tonen verbeterd nut en grotere chromatografische capaciteit voor antilichamen dan de deeltjes die van het materialenoxyde buiten dit gamma vallen. De oxyden van het metaal zoals zirconia, titania en alumina kunnen allen met een multi-lewis basisdeel zoals een organofosfaat ethylenediamine-n, n-Tetra (methylenephosphonic) zuur (EDTPA) worden gewijzigd, om een biocompatibele reinigingsmedia voor te veroorzaken, biomoleculen.