The invention provides a molded composition having improved noise damping
properties, made of a blend of a soft thermoplastic polyether elastomer
and a hard polyester resin reinforced with a fibrous or particulate
filler, the molded composition having an inhomogeneous structure
comprising a surface part which is rich in elastomer and depleted in the
polyester resin and the reinforcing filler compared to its inner part,
obtained by monocomponent injection molding of a blend of the soft and the
hard polyester resin wherein only the polyester resin contains the
reinforcing particulate filler. The molded composition has a flex modulus
Fm in the range 0.5 to 10 GPa, and maintains a sufficient minimum tan
delta damping factor t_ over a temperature range of -50.degree. C. to
170.degree. C.
De uitvinding voorziet een gevormde samenstelling hebben verbeterdd de eigenschappen van de lawaaibevochtiging, die van een mengsel van een zacht thermoplastisch versterkt polyetherelastomeer en een harde polyesterhars worden gemaakt van een vezelige of corpusculaire vuller, de gevormde samenstelling die een niet homogene structuur heeft bestaand uit een oppervlaktedeel dat rijk aan elastomeer is en in de polyesterhars en de versterkende vuller in vergelijking met zijn binnendeel geweest, dat door monocomponent injectie wordt verkregen van een mengsel van de zachte en harde polyesterhars te vormen waarin slechts de polyesterhars de versterkende corpusculaire vuller bevat. De gevormde samenstelling heeft een flex modulus Fm in de waaier 0,5 tot 10 GPa, en handhaaft een voldoende minimumtan deltabevochtigingsfactor t _ over een temperatuurwaaier van -50.degree. C. aan 170.degree. C.