The invention relates to a method for eliminating metal halides which are
present in a liquid or gaseous, organic or non-organic effluent.
According to the invention, the elimination is carried out by absorption
of said metal halides on alumina agglomerates. The inventive method is
characterised in that: the specific surface area of said agglomerates is
between 50 and 350 m.sup.2/g, preferably between 70 and 300 m.sup.2/g
and, better still, between 80 and 250 m.sup.2/g; and the V.sub.80.ANG.
thereof is greater than or equal to 20 ml/100 g, preferably greater than
or equal to 25 ml/100 g, better still greater than or equal to 30 ml/100
g and, optimally, greater than or equal to 35 ml/100 g.
A invenção relaciona-se a um método para eliminar os halides do metal que estão atuais em um líquido ou em um effluent gasoso, orgânico ou non-orgânico. De acordo com a invenção, o elimination é realizado pelo absorption de halides ditos do metal em aglomerados do alumina. O método inventive é caracterizado naquele: a área de superfície específica de aglomerados ditos está entre 50 e 350 m.sup.2/g, preferivelmente entre 70 e 300 m.sup.2/g e, melhore ainda, entre 80 e 250 m.sup.2/g; e o V.sub.80.ANG. é disso mais grande do que ou o igual a 20 ml/100 g, preferivelmente mais grandes do que ou igual a 25 ml/100 g, melhora ainda mais grande do que ou o igual a 30 ml/100 g e, optimally, mais grande do que ou igual a 35 ml/100 g.