A porous metal body having a foam structure of 500 .mu.m or less in average
pore diameter, wherein the skeleton is composed of an alloy primarily
including Fe and Cr, and Cr carbide or FeCr carbide is uniformly dispersed
in the texture. The metal porous body is produced by preparing a slurry
primarily containing an Fe oxide powder having an average particle
diameter of 5 .mu.m or less, at least one powder selected from metallic
Cr, Cr alloys, and Cr oxides, a thermosetting resin, and a diluent,
applying a coating of this slurry to a resin core body having a foam
structure, performing drying, and thereafter, performing firing in a
non-oxidizing atmosphere so as to produce a metal porous body having the
aforementioned skeleton structure.
Ein poröser Metallkörper, der eine Schaumgummistruktur von mu.m 500 oder von kleiner im durchschnittlichen Poredurchmesser hat, worin das Skelett aus einer Legierung hauptsächlich einschließlich F.E. und Cr besteht, und Crkarbid oder FeCr Karbid wird gleichmäßig in der Beschaffenheit zerstreut. Der Metallporöse Körper wird produziert, indem man eine Schmiere vorbereitet, die hauptsächlich ein F.E. Oxidpuder enthält, das einen durchschnittlichen Partikeldurchmesser von mu.m 5 oder von kleiner, mindestens ein Puder vorgewählt wird von den metallischen Cr-, Crlegierungen und von den Croxiden, ein thermostatoplastisches Harz und von einem Verdünnungsmittel hat und eine Schicht dieser Schmiere an einem Harzkernkörper anwendet, der eine Schaumgummistruktur hat und das Trocknen und danach durchführt und Zündung in einer nicht-oxidierenden Atmosphäre durchführt, um einen Metallporösen Körper zu produzieren, der die vorher erwähnte skeleton Struktur hat.