A thermoplastic molding composition comprises a resin composition having 50
to about 90 weight percent of a polyester, about 8 to about 48 weight
percent of a polyetherimide, about 2 to about 25 weight percent of a high
rubber graft impact modifier, each based on the total resin composition,
and up to about 15 weight percent of a particulate filler. A making the
composition comprises pre-melt compounding a polyester, a polyetherimide,
and a high rubber graft impact modifier to form a pre-compounded blend,
wherein the pre-compounded blend has a Tg of greater than or equal to
about 110.degree. C.; and dry-blending a crystallized polyester with the
pre-compounded blend to form the molding composition. Such molding
compositions are particularly useful in blow-molding container for liquids
such as beer.
Uma composição de molde thermoplastic compreende uma composição da resina que tem 50 aos por cento de um poliéster, aproximadamente 8 de aproximadamente 90 pesos aos por cento de um polyetherimide, aproximadamente 2 aos por cento de aproximadamente 25 pesos de um modificador de borracha elevado do impacto do graft, cada um de aproximadamente 48 pesos baseado na composição total da resina, e até por cento de aproximadamente 15 pesos de um enchimento particulate. Fazer a composição compreende pre-derrete combinando um poliéster, um polyetherimide, e um modificador de borracha elevado do impacto do graft para dar forma a uma mistura pre-combinada, wherein a mistura pre-combinada tem um Tg de mais grande do que ou do igual aproximadamente a 110.degree. C.; e seco-misturando um poliéster cristalizado com a mistura pre-combinada para dar forma à composição de molde. Tais composições de molde são particularmente úteis no recipiente do fund-molde para líquidos tais como a cerveja.