The invention relates to a method for purification of metallurgical grade
silicon where a calcium containing compound is added to molten silicon
prior to or after the silicon is tapped from the furnace. The silicon is
cast and solidified at a relatively high cooling rate and the solidified
silicon is crushed and subjected to a purification process consisting of
two leaching steps. In the first leaching step the silicon is treated with
an aqueous solution of FeCl.sub.3 or FeCl.sub.3 and HCl which causes
disintegration of the silicon, and in the second leaching step the silicon
is treated with an aqueous solution of HF or HF/HNO.sub.3.
Calcium-containing compound is added to the molten silicon in an amount
necessary to provide between 0.3 and 0.95% by weight of calcium in the
molten silicon and the weight ratio between Al and Fe in the molten
silicon is regulated to between 0.5 and 2.0 by addition of aluminum to the
molten silicon.
L'invention concerne une méthode pour la purification du silicium métallurgique de catégorie avant où un calcium contenant le composé est ajouté au silicium fondu ou après que le silicium est tapé du four. Le silicium est moulé et solidifié à un taux de refroidissement relativement élevé et au silicium solidifié est écrasé et soumis à une purification de processus se composant de deux étapes de lixiviation. Dans la première étape de lixiviation le silicium est traité avec un soluté de FeCl.sub.3 ou FeCl.sub.3 et HCl qui cause la désintégration du silicium, et dans la deuxième étape de lixiviation le silicium est traité avec un soluté d'à haute fréquence ou de HF/HNO.sub.3. Calcium-contenir le composé est ajouté au silicium fondu dans une quantité nécessaire pour fournir entre 0.3 et 0.95% en poids du calcium dans le silicium fondu et du rapport de poids à Al du Fe dans le silicium fondu est réglé à entre 0.5 et 2.0 par l'addition de l'aluminium au silicium fondu.