A ceramic material containing organic binder is formed by extrusion, dried
and cut off so as to make the honeycomb body 100 having the bulkheads 11
and a plurality of cells 12 partitioned by the bulkheads 11 and
penetrating between both end faces of the honeycomb body 100. The tapered
jig 3 having a tapered forward end portion 31 is inserted into the opening
13 of the cell 12 of the honeycomb body 100. Then, the bulkheads 11 are
heated and softened and deformed by a pushing force given by the tapered
jig 3 so that the opening 13 of the cell 12 is expanded to form the large
opening 131, and the opening 13 of the adjoining cell 12 is reduced at the
same time so as to form the small opening 132. After that, the honeycomb
body 100 is fired. In this way, the exhaust gas purifying filter for
collecting particulates is manufactured.
Un material de cerámica que contiene la carpeta orgánica es formado por la protuberancia, secado y cortado para hacer el cuerpo 100 del panal que tiene los tabiques herméticos 11 y una pluralidad de las células 12 repartidas por los tabiques herméticos 11 y que penetra entre ambas caras del extremo del cuerpo 100 del panal. La plantilla afilada 3 que tiene una parte periférica delantera afilada 31 se inserta en la abertura 13 de la célula 12 del cuerpo 100 del panal. Entonces, los tabiques herméticos 11 son calentados y ablandados y deformidos por una fuerza que empuja dada por la plantilla afilada 3 para ampliar la abertura 13 de la célula 12 para formar la abertura grande 131, y la abertura 13 de la célula colindante 12 esté reducida en el mismo tiempo para formar la abertura pequeña 132. Después de ese, se enciende el cuerpo 100 del panal. De esta manera, el filtro de la purificación del gas de escape para recoger particulates es manufacturado.