The present invention is directed to homo-polymers and copolymers of
mono-1-olefins, a method of making such polymers,and uses of such
polymers. Polymers of the present invention are formed by contacting at
least one mono-1-olefin having from 2 to about 20 carbon atoms per
molecule and at least one mono-1-olefin co-monomer having from 2 to about
10 carbon atoms per molecule in a reaction zone under polymerization
conditions in the presence of a hydrocarbon diluent, a catalyst system,
and a cocatalyst. In another aspect of the present invention, ethylene
copolymers are employed to produce PE-100 pipe. Further, these ethylene
copolymers may be employed to produce PE-100 pipe having both small
diameters and diameters in excess of 42 inches substantially without
sagging or other gravitational deformation. Copolymers of ethylene and
1-hexene are disclosed which are used to produce PE-100 pipe.
Η παρούσα εφεύρεση κατευθύνεται homo-polymers και copolymers των μονο-1-ολεφινών, μια μέθοδος παραγωγής τέτοια πολυμερή σώματα, και χρήσεις τέτοιων πολυμερών σωμάτων. Τα πολυμερή σώματα της παρούσας εφεύρεσης διαμορφώνονται με την επαφή τουλάχιστον μιας μονο-1-ολεφίνης που έχει από 2 σε περίπου 20 άτομα άνθρακα ανά το μόριο και τουλάχιστον ένα co-monomer μονο-1-ολεφινών που έχουν από 2 σε περίπου 10 άτομα άνθρακα ανά μόριο σε μια ζώνη αντίδρασης υπό τους όρους πολυμερισμού παρουσία diluent υδρογονανθράκων, ενός συστήματος καταλυτών, και ενός cocatalyst. Σε μια άλλη πτυχή της παρούσας εφεύρεσης, copolymers αιθυλενίου υιοθετούνται για να παραγάγουν το σωλήνα pe- 100. Περαιτέρω, αυτά τα copolymers αιθυλενίου μπορούν να χρησιμοποιηθούν για να παραγάγουν το σωλήνα pe- 100 που έχει και τις μικρές διαμέτρους και τις διαμέτρους παραπάνω από 42 ίντσες ουσιαστικά χωρίς κρεμώντας ή άλλη βαρύτητας παραμόρφωση. Copolymers του αιθυλενίου και του 1-χεξενε αποκαλύπτονται που χρησιμοποιούνται για να παραγάγουν το σωλήνα pe- 100.