Process for the production of statistic elastomeric conjugated diene-vinyl
arene copolymers having a branched structure which comprises: (1) anionic
copolymerization in solution of the conjugated diene and vinyl arene
monomers, in the presence of randomizing agents and an initiator selected
from the group of Lithium alkyls, the copolymerization being carried out
until the almost total disappearance of the monomers; (2) addition to the
solution of step (1) of a quantity of Lithium alkyl from 1 to 4 times the
molar quantity of the Lithium alkyl of step (1); (3) addition to the
polymeric solution of step (2) of a compound having the general formula
R--Br, the molar ratio between R--Br and the total Lithium alkyl ranging
from 0.6/1 to 1/1, preferably from 0.7/1 to 0.9/1, thus obtaining an
elastomeric branched copolymer.
Proces voor de productie van statistiek elastomeric vervoegde diene-vinylarene copolymeren die een vertakte structuur hebben die bestaat uit: (1) anionische copolymerisatie in oplossing van de vervoegde diene en vinylarene monomeren, in aanwezigheid van het willekeurig verdelen van agenten en een initiatiefnemer die uit de groep Lithium wordt geselecteerd alkyls, de copolymerisatie die tot de bijna totale verdwijning van de monomeren wordt uitgevoerd; (2) toevoeging aan de oplossing van stap (1) van een hoeveelheid alkyl van het Lithium van 1 tot 4 keer de maalhoeveelheid van alkyl van het Lithium van stap (1); (3) toevoeging aan de polymere oplossing van stap (2) van een samenstelling die de algemene formule R -- Br, de maalverhouding tussen R heeft -- Br en totale alkyl die van het Lithium zich van 0,6/1 tot 1/1, bij voorkeur van 0,7/1 tot 0,9/1 uitstrekt, waarbij een elastomeric vertakt copolymeer wordt verkregen.