A Thulium-doped silica fiber normally has its strongest gain at 1.9 microns
and thus is not suitable for communication use. By engineering a W-profile
or depressed cladding fiber with an appropriate index profile having a
fundamental mode cut-off between 1.9 microns and the shorter wavelength of
desired operation, an optical amplifier based on the W-profile
Thulium-doped silica fiber operates at wavelengths shorter than
conventional amplifiers, just above what is currently called the Erbium
L-band. In a preferred embodiment, the cut-off wavelength is at or near
1.7 .mu.m, eliminating longer wavelengths from the fiber. Amplifiers
engineered according to the principles and techniques of the present
invention can operate in the wavelength range between about 1.6 to 1.8
microns, which is particularly useful for telecommunications.
Eine Thulium-lackierte Silikonfaser hat normalerweise seinen stärksten Gewinn bei 1.9 Mikrons und ist folglich nicht für Kommunikation Gebrauch verwendbar. Indem er ein W-Profil oder niedergedrückte eine Umhüllungfaser mit einem passenden Indexprofil ausführt, das eine grundlegende Modusabkürzung zwischen 1.9 Mikrons und der kürzeren Wellenlänge des gewünschten Betriebes hat, funktioniert ein optischer Verstärker, der auf der W-Profil Thulium-lackierten Silikonfaser basiert, herkömmlichen Verstärkern der Wellenlängen an den kürzer als, gerade über, was z.Z. das Erbium L-Band genannt wird. In einer bevorzugten Verkörperung ist die Grenzwellenlänge oder nahe am mu.m 1.7 und beseitigt längere Wellenlängen von der Faser. Die Verstärker, die entsprechend den Grundregeln und den Techniken der anwesenden Erfindung ausgeführt werden, können im Wellenlängenbereich zwischen ungefähr 1.6 bis 1.8 Mikrons funktionieren, der für Nachrichtentechniken besonders nützlich ist.