A PET hot fill bottle (2) has a neck (3) and a body (4). It is stretched
and blown into a cavity (14), with internal pressure holding the body
against the cavity. During a first period, the cavity is heated to
100.degree. to 160.degree. C. for between 3 to 7 seconds to relax stresses
in the body. During a second period the cavity is cooled to 60.degree. to
120.degree. C. for 4 to 8 seconds. This solidifies it--without introducing
stresses--so that it can be removed from the mould. The resulting bottle
is heat stable when filled with water close to its boiling point, namely
at 92.degree. C. to 98.degree. C. For the rapid heating and cooling of the
mould cavity, it is provided with two series of passages (16, 17). The
former house ohmic heaters (18); whilst the latter are connected to water
and air supply lines (19, 20).
Ένα PET καυτό γεμίζει το μπουκάλι (2) έχει έναν λαιμό (3) και ένα σώμα (4). Τεντώνεται και φυσιέται σε μια κοιλότητα (14), με την εσωτερική πίεση που κρατά το σώμα ενάντια στην κοιλότητα. Κατά τη διάρκεια μιας πρώτης περιόδου, η κοιλότητα θερμαίνεται σε 100.degree. σε 160.degree. Γ. για μεταξύ 3 έως 7 δευτερόλεπτα για να χαλαρώσει τις πιέσεις στο σώμα. Κατά τη διάρκεια μιας δεύτερης περιόδου η κοιλότητα δροσίζεται σε 60.degree. σε 120.degree. Γ. για 4 έως 8 δευτερόλεπτα. Αυτό το σταθεροποιεί -- χωρίς εισαγωγή τονίζει -- έτσι ώστε μπορεί να αφαιρεθεί από τη φόρμα. Το προκύπτον μπουκάλι είναι σταύλος θερμότητας όταν γεμίζεται με το ύδωρ κοντά στο σημείο βρασμού του, δηλαδή σε 92.degree. Γ. σε 98.degree. γ. Για τη γρήγορη θέρμανση και την ψύξη της κοιλότητας φορμών, παρέχεται δύο σειρές μεταβάσεων (16, 17). Τα πρώτα στεγάζουν τις ωμικές θερμάστρες (18) ενώ τα τελευταία συνδέονται με τις γραμμές ύδατος και παροχής αέρα (19, 20).