A process for making a composite product in which reinforcement fibers are
subjected to a composition based on a thermohardening resin and a
photoinitiator appropriate to the irradiation by which the composition is
to be treated. The resulting pre-impregnated material is introduced into a
prepolymerization device, in which the pre-impregnated material is
prepolymerized by appropriate irradiation. Lengths of the precomposite are
applied to a support, the shape of which is dictated by the shape of one
face of the composite part which is to be made, and are stacked one on
another in a suitable number and placed snugly against the shape of the
support, and the stack is subjected to final molding at a suitable
pressure and temperature in order to polymerize the resin and to join the
different lengths of precomposite.
Μια διαδικασία για ένα σύνθετο προϊόν στο οποίο οι ίνες ενίσχυσης υποβάλλονται σε μια σύνθεση βασισμένη σε μια θερμοσκληρυντική ρητίνη και ένα photoinitiator αρμόδιες για την ακτινοβολία από την οποία η σύνθεση πρόκειται να αντιμετωπιστεί. Το προκύπτον pre-impregnated υλικό εισάγεται σε μια συσκευή prepolymerization, στην οποία το pre-impregnated υλικό είναι από την κατάλληλη ακτινοβολία. Τα μήκη του precomposite εφαρμόζονται σε μια υποστήριξη, η μορφή της οποίας υπαγορεύεται από τη μορφή ενός προσώπου του σύνθετου μέρους που πρόκειται να γίνει, και είναι συσσωρευμένο ένα σε άλλο σε έναν κατάλληλο αριθμό και τοποθετημένος βολικά ενάντια στη μορφή της υποστήριξης, και ο σωρός υποβάλλεται στην τελική σχηματοποίηση σε μια κατάλληλες πίεση και μια θερμοκρασία προκειμένου να πολυμεριστεί η ρητίνη και για να ενώσει τα διαφορετικά μήκη του precomposite.