The present invention relates to a silver braze alloy having improved wetting properties. The silver braze alloy consists essentially of from about 52.25 wt % to about 57.0 wt % silver, from about 38.95 to about 43.0 wt % copper, from about 0.5 wt % to about 5.5 wt %, preferably from about 1.0 wt % to about 5.5 wt %, manganese, and up to about 2.5 wt %, preferably from about 1.5 wt % to about 2.5 wt %, nickel. The alloy further may contain 0.15 wt % total of other trace elements.