A polypropylene resin composition comprises (A) (a-1) a specific crystalline propylene/ethylene block copolymer or (a-3) a polymer mixture comprising the (a-1) and (a-2) a specific crystalline propylene-homopolymer in specific ratio, in an amount of 5 to 56% by weight, (B) a hydroxyl group-containing polypropylene having an intrinsic viscosity [.eta.] of 0.8 to 2.0 dl/g and a melting point of 150 to 168.degree. C., in an amount of 10 to 45% by weight, (C) a copolymer rubber of ethylene and an .alpha.-olefin having a melt flow rate (ASTM D-1238, 230.degree. C., load of 2160 g) of 0.5 to 15 g/10 min, in an amount of 18 to 25% by weight, (D) a hydrogenation product of a block copolymer containing a polymer block of a monovinyl-substituted aromatic hydrocarbon compound and a polymer block of a conjugated diene compound, in an amount of 1 to 10% by weight, and (E) an inorganic filler in an amount of 15 to 25% by weight, the total amount of said components (A), (B), (C), (D) and (E) being 100% by weight, hydroxyl group-containing monomer units derived from the hydroxyl group-containing polypropylene (B) being contained in amounts of 1.3 to 4.0% by weight in 100% by weight of the polypropylene resin composition. The polypropylene resin composition exhibits excellent coating adhesion properties and has excellent processability and mechanical strength with a good balance.