Problem To offer a suitable polyether imide resin composition for the
plastic components for automobiles, domestic appliances or OA apparatus,
equipment's for media where heat resistance, dimensional stability and
fire retardancy is required. Means for solving the problem Filler
reinforced polyether imide resin composition is characterized by
containing (A) polyether imide resin, (B) thermoplastic resin, (C)
fibrous reinforced filler and (D) Non-fibrous inorganic filler, wherein
the amount of (A) polyether imide resin is 1 to 95% by weight, (B)
thermoplastic resin: 1 to 95% by weight, (C) fibrous reinforced filler: 2
to 80% by weight, (D) Non-fibrous inorganic filler: 2 to 80% by weight,
when total of (A) to (D) is 100% by weight. The filler reinforced
polyether imide resin composition contains (A) polyether imide resin, (B)
thermoplastic resin, (C) fibrous reinforced filler, (D) Non-fibrous
inorganic filler and (E) alkali earth metal salts, wherein the amount of
(A) polyether imide resin: 1 to 95% by weight, (B) thermoplastic resin: 1
to 95% by weight, (C) fibrous type reinforced filler: 2 to 80% by weight,
(E) non-fibrous inorganic filler. 2 to 80% by weight, when total of (A)
to (D) is 100% by weight, and (E) alkali earth metal salts are included
in the amount of 0 to less than 5 parts by weight.