Using novel synthetic techniques, siloxane-urea segmented copolymers are made. The copolymers advantageously contain a polyether interface, with controlled morphologies and properties. High molecular weight, high strength siloxane-urea copolymers with urea hard segment contents ranging from 5 to over 60% by weight may be prepared. Polymer properties that can independently be controlled include modulus (1.0 to 120 MPa), ultimate tensile strength (1.5 to 25 MPa), level of equilibrium water absorption (.about.0 to 100% by weight) and refractive index (1.43 to 1.46).