Polyamide polyalkyl(meth)acrylate block copolymers which are built from
polyamide generating monomers in addition to 15-70 weight percent
polyalkyl(meth)acrylates as well as products produced from same. The
block copolymers are produced by producing polyamide or copolyamide
blocks with an average molar mass in the range between 500 and 5,000
g/Mol with an amino end group in a first polymerization or
polycondensation step and degassing in order to reduce the water content;
adding, in a second step, .alpha.,.omega.-functionalized
polyalkyl(meth)acrylate diols; and fully condensing the reaction mixture
into high-molecular block copolymer (A) at a reduce pressure in a further
polycondensation step; discharging it, or further processing it into
molding bodies.