The present invention provides a steel sheet excellent in workability,
which may be used for components of an automobile or the like, and a
method for producing the same. More specifically, according to one
exemplary embodiment of the present invention, a steel sheet excellent in
workability, including in mass, 0.08 to 0.25% C, 0.001 to 1.5% Si, 0.01
to 2.0% Mn, 0.001 to 0.06% P, at most 0.05% S, 0.001 to 0.007% N, 0.008
to 0.2% Al, at least 0.01% Fe. The steel sheet having an average r-value
of at least 1.2, an r-value in the rolling direction of at least 1.3, an
r-value in the direction of 45 degrees to the rolling direction of at
least 0.9, and an r-value in the direction of a right angle to the
rolling direction of at least 1.2.