The invention provides a process for the preparation of a thermoplastic elastomeric resin composition comprising melt kneading (a) 100 parts by weight of a block copolymer consisting of at least two polymeric blocks (A) composed mainly of a vinyl aromatic compound and at least one polymeric block (B) composed mainly of a conjugated diene compound, and/or a hydrogenated block copolymer obtained by hydrogenating said block copolymer, (b) 40 to 240 parts by weight of a non-aromatic softening agent for rubber, (c) 5 to 300 parts by weight of polyethylene or a copolymer composed mainly of ethylene, and (d) 5 to 60 parts by weight of polypropylene or a copolymer composed mainly of propylene, characterized in that the process comprises the following steps: (I) melt kneading the whole amounts of components (a), (b) and (d) and a part of component (c), and, at the same time or subsequently, melt kneading these with (f) an organic peroxide, and (II) melt kneading the product obtained from step (I) with the remaining part of component (c), and component (c) is one which has been prepared using a single site catalyst. The obtained composition is soft and excellent in heat deformation resistance and mechanical strength, moldability and processability. The present invention also provide a thermoplastic elastomeric resin composition comprising the above components (a), (c) and (d) in an amount of 100 parts by weight, 5 to 150 parts by weight and 5 to 80 parts by weight, respectively. The composition is soft and excellent in heat deformation resistance and mechanical strength, moldability and processability and shows good results in the extraction tests.

A invenção fornece um processo para a preparação de uma composição elastomeric thermoplastic da resina que compreende o derretimento que kneading (a) 100 porções pelo peso de um copolymer do bloco que consiste ao menos em dois blocos polymeric (A) compostos principalmente de um composto aromatic do vinil e ao menos de um bloco polymeric (B) compostos principalmente de um composto conjugated do diene, e/ou um copolymer hydrogenated do bloco obtido hydrogenating o copolymer dito do bloco, peças pelo peso de um agente amaciando non-aromatic para a borracha, as peças peças de (b) 40 a 240 de (c) 5 a 300 pelo peso do polietileno ou por um copolymer composto principalmente do etileno, e de (d) 5 a 60 pelo peso do polypropylene ou por um copolymer composto principalmente do propylene, caracterizado em que o processo compreende as seguintes etapas: (I) o derretimento que kneading as quantidades inteiras de componentes (a), (b) e (d) e uma peça do componente (c), e, ao mesmo tempo ou subseqüentemente, do derretimento que kneading estes com (f) um peroxide orgânico, e (ii) o derretimento que kneading o produto obtido da etapa (I) com a parte restante do componente (c), e do componente (c) é um que foi preparado usando um único catalizador do local. A composição obtida é macia e excelente na resistência da deformação do calor e força, moldability e processability mecânicos. A invenção atual fornece também uma composição elastomeric thermoplastic da resina que compreende os componentes acima (a), (c) e (d) em uma quantidade de 100 porções pelo peso, 5 a 150 porções pelo peso e 5 a 80 porções pelo peso, respectivamente. A composição é macia e excelente na resistência da deformação do calor e força mecânica, moldability e processability e resultados bons das mostras nos testes da extração.