The present invention provides a ferritic stainless steel sheet having excellent formability and excellent surface quality after forming. In specific means, the steel sheet contains, by mass %, 0.02 to 0.06% of C, 1.0% or less of Si, 1.0% or less of Mn, 0.05% or less of P, 0.01% or less of S, 0.005% or less of Al, 0.005% or less of Ti, 11 to 30% of Cr, 0.7% or less of Ni, the balance composed of Fe, and inevitable impurities, wherein N is contained to satisfy the relation to the C content represented by 0.06.ltoreq.(C+N).ltoreq.0.12, and 1.ltoreq.N/C, and V is contained to satisfy the relation to the N content represented by 1.5.times.10.sup.-3.ltoreq.(V.times.N).ltoreq.1.5.times.10.sup.-2 (wherein C, N and V: the contents (mass %) of the elements).

La présente invention fournit une feuille de ferrite d'acier inoxydable ayant l'excellent formability et l'excellente qualité extérieure après la formation. Dans des moyens spécifiques, la tôle d'acier contient, par % de masse, 0.02 à 0.06% de C, 1.0% ou moins de silicium, 1.0% ou moins de manganèse, 0.05% ou moins de P, 0.01% ou moins de S, 0.005% ou moins d'Al, 0.005% ou moins de Ti, 11 à 30% de Cr, 0.7% ou moins de Ni, l'équilibre composé de Fe, et les impuretés inévitables, où N est contenu pour satisfaire la relation au contenu de C représenté par 0.06.ltoreq.(C+N).ltoreq.0.12, et le 1.ltoreq.N/C, et V est contenu pour satisfaire la relation à la teneur en n représentée par 1.5.times.10.sup.-3.ltoreq.(V.times.N).ltoreq.1.5.times.10.sup.-2 (où C, N et V : les teneurs (% de masse) des éléments).