A hot rolled electromagnetic steel sheet having excellent magnetic properties and corrosion resistance is obtained by heating a super-high purity iron comprising Fe: not less than 99.95 mass %, C+N+S: not more than 10 mass ppm, O: not more than 50 mass ppm and the remainder being inevitable impurity to .gamma.-zone and subjecting in this .gamma.-zone to hot rolling at a total rolling reduction of not less than 50% and under condition that at least one pass is a friction coefficient between roll and rolling material of not more than 0.3 and thereafter cooling at an average cooling rate of 0.5.about.150.degree. C. over Ar.sub.3 transformation point .about.300.degree. C.

Une tôle d'acier électromagnétique laminée à chaud ayant d'excellentes propriétés magnétiques et résistance à la corrosion est obtenue en chauffant un superbe-haut fer de pureté comportant le Fe : pas moins de 99.95 % de masse, C+N+S : pas plus de 10 pages par minute de masse, O : pas plus de 50 pages par minute de masse et le reste étant gamma.-zone inévitable d'impureté et soumettant dans cette gamma.-zone au roulement chaud à une réduction totale de roulement pas moins de de 50% et dans la condition qu'au moins un passage est un coefficient de frottement entre le roulement et le matériel de roulement pas plus de de 0.3 et se refroidir ensuite à un taux de refroidissement moyen de 0.5.about.150.degree. About.300.degree fini de point de la transformation Ar.sub.3 de C.. C.