A porous material suitable for use in a bearing rolling element. The porous material is obtained by a process which includes mixing degreased bran derived from rice bran with a thermosetting resin before kneading, subjecting a kneaded mixture to a primary firing in an inert gas at a temperature in a range of 700 to 100.degree. C., pulverizing the kneaded mixture after the primary firing into carbonized powders sieved through a screen of 100-mesh, mixing the carbonized powders or the carbonized powders and ceramic powders with a thermosetting resin before kneading, pressure-forming a kneaded mixture thus obtained at a pressure in a range of 20 to 30 MPa, and applying a heat treatment again to a formed kneaded mixture in the inert gas at a temperature in a range of 100 to 1100.degree. C.

Um apropriado material poroso para o uso em um elemento do rolling do rolamento. O material poroso é obtido por um processo que inclua o farelo desengraxado misturando derivado do farelo de arroz com uma resina thermosetting antes de kneading, sujeitando uma mistura kneaded a um acendimento preliminar em um gás inerte em uma temperatura em uma escala de 700 a 100.degree. C., pulverizing a mistura kneaded após o acendimento preliminar em pós carbonizados sieved através de uma tela de 100-mesh, misturando os pós carbonizados ou os pós carbonizados e pós cerâmicos com uma resina thermosetting antes de kneading, de pressão-dar forma a uma mistura kneaded obtida assim em uma pressão em uma escala de 20 a 30 MPa, e de aplicar um tratamento de calor outra vez a uma mistura kneaded dada forma no gás inerte em uma temperatura em uma escala de 100 a 1100.degree. C.

 
Web www.patentalert.com

< Very high purity fine powders and methods to produce such powders

< Catalyst body and process for breaking down nitrogen oxides

> Preferential oxidation catalyst

> Nanocomposite for fuel cell bipolar plate

~ 00073