Disclosed is an Fe--Ni alloy consisting of, by mass, 30 to 50% of Ni (or 27
to 47% Ni and not more than 22% Co), 0.005 to 0.1% of Nb, less than 0.01%
of C, 0.002 to 0.02% of N, and the balance of Fe and inevitable
impurities, wherein the equation
"0.000013.ltoreq.(% Nb).times.(% N).ltoreq.0.002",
is fulfilled. In the alloy, preferably, the maximum grain size of compounds
primarily containing Nb and nitrogen and other compounds primarily
containing Nb and C is less than 0.5 .mu.m, which can be observed at an
fractional section of metal structure, and a total number of the compounds
is not less than 50,000/mm.sup.2 at an fractional section. An average
grain size of the alloy structure is not less than 10 by the crystal grain
size number as defined in JIS G0551. The alloy may applied to shadow masks
for the Braun tube and lead frames for semiconductor elements.
É divulgado um Fe -- a liga do Ni que consiste, pela massa, em 30 a 50% do Ni (ou o Ni de 27 a de 47% e não mais de 22% Co), em 0.005 a 0.1% do Nb, menos de 0.01% de C, 0.002 a 0.02% de N, e o contrapeso do Fe e de impurezas inevitáveis, wherein a equação "0.000013.ltoreq.(% Nb).times.(% N).ltoreq.0.002", é cumprida. Na liga, preferivelmente, no tamanho de grão máximo dos compostos primeiramente conter o Nb e o nitrogênio e em outro combina primeiramente conter o Nb e C é menos de 0.5 mu.m, que pode ser observado em uma seção fracionária da estrutura do metal, e um número total dos compostos não são menos do que 50,000/mm.sup.2 em uma seção fracionária. Um tamanho de grão médio da estrutura da liga não é menos de 10 pelo número de cristal do tamanho de grão como definido em JIS G0551. A liga pode aplicado sombrear máscaras para o tubo de Braun e frames da ligação para elementos do semicondutor.