The non-oriented electrical steel sheet having the following chemical composition: C: 0.01% or less, Si: 2.5% or less, Mn: 2% or less, Al: 1 to 5%, Si+Al+0.5.times.Mn: 2.5 to 5%, with a sheet thickness of 0.1 to 0.4 mm, an average grain diameter of 50 to 180 .mu.m and a Vickers hardness of 130 to 210. The steel sheet is excellent in workability such as punchability and interlocking performance for forming it into cores for motors and also has a lower iron loss and higher magnetic flux density, and thus when used as a core in a motor, achieves the high a motor efficiency. The steel sheet is particularly suitable as a material for cores in inverter-controlled motors.

La lamiera di acciaio elettrica non orientata che ha la seguente composizione chimica: C: 0.01% o di meno, silicone: 2.5% o di meno, manganese: 2% o di meno, Al: 1 - 5%, Si+Al+0.5.times.Mn: 2.5 - 5%, con uno spessore del foglio di 0.1 - 0.4 millimetri, di un diametro medio del grano di mu.m 50 - 180 e di una durezza di Vickers di 130 - 210. La lamiera di acciaio è eccellente in workability quali il punchability e le prestazioni di collegamento per formarle nei nuclei per i motori ed inoltre ha una perdita più bassa del ferro e un'più alta densità magnetica di cambiamento continuo e così una volta usato come nucleo in un motore, realizza il high un'efficienza del motore. La lamiera di acciaio è particolarmente adatta come materiale per i nuclei in motori invertitore-controllati.