A glass or glass powder is fused from a starting mixture containing
approximately 38 wt % to 48 wt % SO.sub.2, 15 wt % to 19 wt % Al.sub.2
O.sub.3, 4.5 wt % to 11 wt % TiO.sub.2, 0 wt % to 1.5 wt % Na.sub.2 O, 0
wt % to 1.5 wt % K.sub.2 O and 23 wt % to 30 wt % CaO. In addition, a
glass powder mixture includes two glass powders, a carbon black powder and
an organic binder, the first glass powder having a mean particle size of
approximately 150 .mu.m to 250 .mu.m, the second glass powder having a
mean particle size of less than approximately 100 .mu.m, which may be 10
.mu.m to 70 .mu.m. The glass or glass powder mixture is suitable for
producing a glass ceramic, such as that used as a resistor seal and/or a
gas-tight glass ceramic solder in a spark plug.
Een glas of een glaspoeder worden gesmolten van een beginnend mengsel dat ongeveer 38 % gew. aan 48 % gew. SO.sub.2, 15 % gew. bevat aan 19 % gew. Al.sub.2 O.sub.3, 4,5 % gew. aan 11 % gew. TiO.sub.2, 0 % gew. aan 1,5 % gew. Na.sub.2 O, 0 % gew. aan 1,5 % gew. K.sub.2 O en 23 % gew. aan 30 % gew. CaO. Bovendien omvat een mengsel van het glaspoeder twee glaspoeder, een zwartselpoeder en een organisch bindmiddel, het eerste glaspoeder die een gemiddelde deeltjesgrootte van mu.m ongeveer 150 hebben aan 250 mu.m, het tweede glaspoeder die een gemiddelde deeltjesgrootte van minder hebben dan mu.m ongeveer 100, die 10 kan zijn mu.m aan mu.m. 70 Het glas of van het glaspoeder mengsel is geschikt om een glas te produceren ceramisch, zoals dat gebruikt als weerstandsverbinding en/of gasdicht glas ceramisch soldeersel in een vonkenstop.