The invention relates to a new process for the preparation of precipitated
silica which has an excellent dispersibility and very satisfactory
reinforcing properties. It also relates to new precipitated silicas which
are in the form of powder, of substantially spherical beads or of
granules, these silicas being characterized by the fact that they have a
CTAB specific surface of between 140 and 200 m.sup.2 /g, a BET specific
surface of between 140 and 200 m.sup.2 /g, a DOP oil uptake lower than 300
ml/100 g, a median diameter, after disintegration with ultrasound, smaller
than 3 .mu.m, an ultrasonic disintegration factor higher than 10 ml and an
aluminum content of at least 0.35% by weight. The invention also relates
to the use of the said silicas as reinforcing fillers for elastomers.
La invención se relaciona con un nuevo proceso para la preparación de la silicona precipitada que tiene una dispersabilidad excelente y características que refuerzan muy satisfactorias. También se relaciona con las siliconas precipitadas nuevas que están en la forma de polvo, de granos substancialmente esféricos o de gránulos, estas siliconas que son caracterizadas por el hecho de que tienen una superficie específica del CTAB entre de 140 y 200 m.sup.2 /g, una superficie específica de la APUESTA entre de 140 y 200 m.sup.2 /g, un uptake de aceite del DOP más bajo de 300 ml/100 g, un diámetro mediano, después de la desintegración con ultrasonido, más pequeño el mu.m de 3, un factor ultrasónico de la desintegración más arriba de 10 ml y un contenido de aluminio de por lo menos 0.35% al lado del peso. La invención también se relaciona con el uso de las siliconas dichas como reforzar los llenadores para los elastomers.