An object of the present invention is to provide a hot-dip galvanized steel
sheet which is excellent in adhesion with a hot-dip galvanized zinc layer,
and has high tensile strength and good formability even when a steel sheet
containing Si and Mn in relatively larger amounts is used as a basis steel
sheet. The hot-dip galvanized steel sheet is composed of: a basis steel
sheet containing Si in an amount of 0.05 to 2.5% and Mn in an amount of
0.2 to 3%, by mass; a Fe plated layer formed on the basis steel sheet; and
a hot-dip galvanized zinc layer formed on the surface layer of the basis
steel sheet via the Fe plated layer, wherein oxides containing Si and/or
Mn are discontinuously dispersed in the vicinity of the interface between
the basis steel sheet and the Fe plated layer.
Un objeto de la actual invención es proporcionar caliente-sumerge la hoja de acero galvanizada que es excelente en la adherencia con caliente-sumerge capa galvanizada del cinc, y tiene alta fuerza extensible y buen formability incluso cuando una hoja de acero que contiene el silicio y el manganeso en cantidades relativamente más grandes se utiliza como hoja de acero de la base. Caliente-sumerja la hoja de acero galvanizada se compone de: una hoja de acero de la base que contiene el silicio en una cantidad de 0.05 a de 2.5% y de manganeso en una cantidad de 0.2 a el 3%, por la masa; un FE plateó la capa formada en la hoja de acero de la base; y caliente-sumerja la capa galvanizada del cinc formada en la capa superficial de la hoja de acero de la base vía la capa plateada FE, en donde los óxidos que contienen el silicio y/o el manganeso discontinuo se dispersan en la vecindad del interfaz entre la hoja de acero de la base y la capa plateada FE.