An absorbent fibrous foam composite comprising a fluid intake capacity of
at least 15 g/g, a vertical wicking distance of at least 10 cm, and an
absorbency under zero load of at least 15 g/g. The absorbent fibrous foam
composite comprising a water insoluble fibrous material and a
superabsorbent material. The absorbent fibrous foam composite made by
forming a slurry of water, a water-insoluble fiber, and a binding agent. A
water-swellable, water-insoluble superabsorbent material is added to the
slurry and the temperature is lowered until the water freezes. The frozen
water is then removed by sublimation process and an absorbent fibrous foam
recovered. The Gelation Time, which represents a fluid absorption rate of
superabsorbent during the preparation, is critical to preparing uniform
absorbent freeze-dried foams and can be adjusted by various mixing
conditions and physical and chemical superabsorbent treatments.
Absorbent волосистая смесь пены состоя из жидкой пропускной способности при приеме по крайней мере 15 g/g, вертикального wicking расстояния по крайней мере 10 сантиметров, и absorbency под zero нагрузкой по крайней мере 15 g/g. Absorbent волосистая смесь пены состоя из материала воды неразрешимого волосистого и superabsorbent материала. Absorbent волосистая смесь пены сделанная путем формировать slurry воды, воднонерастворимого волокна, и binding вещества. Вод-water-swellable, воднонерастворимый superabsorbent материал добавлен к slurry и температура понижена до тех пор пока вода не замерзнуть. Замороженная вода после этого извлекается процессом сублимации и absorbent волосистая пена взята. Время студневания, которое представляет жидкий тариф абсорбциы superabsorbent во время подготовки, критически к подготовлять равномерное freeze-dried absorbent пенится и можется быть отрегулировано различными смешивая условиями и физическими и химически superabsorbent обработками.