This invention relates generally to a method for growing carbon fiber from
single-wall carbon nanotube (SWNT) molecular arrays. In one embodiment,
the present invention involves a macroscopic molecular array of at least
about 10.sup.6 tubular carbon molecules in generally parallel orientation
and having substantially similar lengths in the range of from about 50 to
about 500 nanometers. The hemispheric fullerene cap is removed from the
upper ends of the tubular carbon molecules in the array. The upper ends of
the tubular carbon molecules in the array are then contacted with a
catalytic metal. A gaseous source of carbon is supplied to the end of the
array while localized energy is applied to the end of the array in order
to heat the end to a temperature in the range of about 500.degree. C. to
about 1300.degree. C. The growing carbon fiber is continuously recovered.
Questa invenzione si riferisce generalmente ad un metodo per la crescita della fibra del carbonio dagli allineamenti molecolari a parete semplice del nanotube del carbonio (SWNT). In un incorporamento, la presente invenzione coinvolge un allineamento molecolare macroscopico almeno circa delle molecole tubolari del carbonio 10.sup.6 nell'orientamento generalmente parallelo ed in avere lunghezze sostanzialmente simili nella gamma di circa 50 a circa 500 nanometri. La protezione emisferica del fullerene è rimossa dalle estremità superiori delle molecole tubolari del carbonio nell'allineamento. Le estremità superiori delle molecole tubolari del carbonio nell'allineamento allora si mettono in contatto con con un metallo catalitico. Una fonte gassosa di carbonio è fornita alla conclusione dell'allineamento mentre l'energia localizzata è applicata alla conclusione dell'allineamento per riscaldare l'estremità ad una temperatura all'incirca 500.degree. C. circa a 1300.degree. C. La fibra crescente del carbonio è recuperata continuamente.