A copper alloy that consists essentially of, by weight, from 0.15% to 0.7%
of chromium, from 0.005% to 0.3% of silver, from 0.01% to 0.15% of
titanium, from 0.01% to 0.10% of silicon, up to 0.2% of iron, up to 0.5%
of tin, and the balance copper and inevitable impurities has high
strength, a yield strength in excess of 80 ksi, and high electrical
conductivity, in excess of 80% IACS. The alloy further has substantially
isotropic bend characteristics when the processing route includes a
solution heat anneal above 850.degree. C. and subsequent cold rolling into
sheet, strip or foil interspersed by bell annealing. As a result, the
alloy is particularly suited for forming into box-type electrical
connectors for both automotive or multimedia applications. The alloy is
also suitable for forming into a rod, wire or section.
Una aleación de cobre en la cual consiste esencialmente, al lado del peso, a partir la 0.15% a 0.7% de cromo, a partir la 0.005% a 0.3% de plata, a partir la 0.01% a 0.15% del titanio, a partir la 0.01% a 0.10% de silicio, hasta 0.2% de hierro, hasta 0.5% de lata, y el cobre del balance y las impurezas inevitables tiene alta fuerza, una fuerza de la producción en el exceso del ksi 80, y alta conductividad eléctrica, en el exceso de el 80% IACS. La aleación más futura tiene características substancialmente isotrópicas de la curva cuando la ruta de proceso incluye un calor de la solución recuece sobre 850.degree. C. y balanceo frío subsecuente en la hoja, la tira o la hoja entremezclada por el recocido de la campana. Consecuentemente, la aleación se satisface particularmente para formar en los empalmes eléctricos encajonados para los usos automotores o de las multimedias. La aleación es también conveniente para formar en una barra, un alambre o una sección.