A killed and vacuum-degassed very-low-carbon steel containing, by weight,
between 0.10 and 0.35% manganese, less than 0.006% nitrogen, less than
0.025% phosphorus, less than 0.020% sulphur, less than 0.020% silicon, at
most 0.08% of at least one of the elements copper, nickel and chromium, as
well as aluminum. The steel is cast in the form of a slab, the slab is hot
rolled in order to obtain a hot-rolled sheet, the hot-rolled sheet is
coiled, the hot-rolled sheet is cold rolled in two rolling operations
separated by a continuous annealing operation. The steel contains at most
0.006% carbon by weight and 0.010% aluminum and the hot-rolled sheet is
coiled at a temperature below 620.degree. C. Preferably, the steel is
killed by mixing with a slag containing adjusted amounts of aluminum and
of alumina.
Ein getöteter und Vakuum-entgaster Sehr-niedrigcarbon, der Stahl ist, nach Gewicht, zwischen 0.10 und 0.35% Mangan, weniger als 0.006% Stickstoff, weniger als 0.025% Phosphor, weniger als 0.020% Schwefel, weniger als 0.020% Silikon enthalten, höchstens 0.08% von einem mindestens der Elemente, verkupfert, Nickel und Chrom, sowie Aluminium. Der Stahl wird in Form einer Platte geworfen, die Platte ist warm gewalzt, um ein warm gewalztes Blatt zu erhalten, das warm gewalzte Blatt ist aufgerollt, das warm gewalzte Blatt wird kaltgewalzt in zwei rollenden Betrieben, die durch einen ununterbrochenen Ausglühenbetrieb getrennt werden. Der Stahl enthält höchstens 0.006% Carbon nach Gewicht und 0.010% Aluminium und das warm gewalzte Blatt ist bei einer Temperatur unter 620.degree aufgerollt. C. Vorzugsweise wird der Stahl getötet, indem man mit einer Schlacke mischt, die justierte Aluminiummengen und Tonerde enthält.