Disclosed is a free-cutting steel for machine structural use which always
exhibits desired machinability, particularly, machinability by cutting
with cemented carbide tools. This free-cutting steel is produced by
preparing a molten alloy of the composition consisting essentially of, by
weight %, C: 0.05-0.8%, Si: 0.01-2.5%, Mn: 0.1-3.5% and O: 0.0005-0.01%,
the balance being Fe and inevitable, and adjusting the addition amounts of
Al and Ca in such a manner as to satisfy the above ranges, S: 0.01-0.2%,
Al: 0.001-0.020% and Ca: 0.0005-0.02%, and the conditions of [S]/[O]: 8-40
[Ca].times.[S]: 1.times.10.sup.-5 -1.times.10.sup.-3 [Ca]/[S]: 0.01-20 and
[Al]: 0.001-0.020% to obtain a steel characterized in that the area in
microscopic field occupied by the sulfide inclusions containing Ca of 1.0%
or more neighboring to oxide inclusions containing CaO of 8-62% is
2.0.times.10.sup.-4 mm.sup.2 or more per 3.5 mm.sup.2.
È rilevato un acciaio free-cutting per uso strutturale della macchina che esibisce sempre la fabbricabilità voluta, specialmente, fabbricabilità tagliando con gli attrezzi cementati del carburo. Questo acciaio free-cutting è prodotto preparando una lega fusa della composizione che è costituita essenzialmente da, di peso %, C: 0.05-0.8%, silicone: 0.01-2.5%, manganese: 0.1-3.5% ed O: 0.0005-0.01%, l'equilibrio che è Fe ed inevitabile e registrante gli importi dell'aggiunta di Al e CA in un tal modo quanto a soddisfano le suddette gamme, S: 0.01-0.2%, Al: 0.001-0.020% e CA: 0.0005-0.02% ed i termini di [ S]/[O ]: 8-40 [ Ca].times.[S ]: 1.times.10.sup.-5 -1.times.10.sup.-3 [ Ca]/[S ]: 0.01-20 e [ Al ]: 0.001-0.020% per ottenere un acciaio caratterizzato dal fatto che la zona nel campo microscopico occupato tramite le inclusioni del solfuro che contengono un CA di 1.0% o più vicino alle inclusioni dell'ossido che contengono un cao di 8-62% è 2.0.times.10.sup.-4 mm.sup.2 o più per 3.5 mm.sup.2.