Bimetal saw band comprising a support band of high microstructural
stability and fatigue strength, comprising 0.25 to 0.35% of carbon, 0.3 to
0.5% of silicon, 0.8 to 1.5% of manganese, 1.0 to 2.0% of molybdenum, 1.5
to 3.5% of chromium, 0.5 to 1.5% of nickel, 0.5 to 2.5% of tungsten, 0.15
to 0.30% of vanadium, 0.05 to 0.10% of niobium, 0.05 to 1.0% of copper, up
to 0.2% of aluminum, up to 1% of cobalt, remainder iron including
melting-related impurities, and tooth tips made from a steel with high
wear resistance, comprising 1.0 to 2.0% of carbon, 3 to 6% of chromium, 1
to 5% of vanadium, 3 to 10% of molybdenum, 4 to 10% of tungsten, 4 to 10%
of cobalt, up to 1% of silicon, up to 1% of manganese, up to 0.5% of
niobium, up to 0.5% of nitrogen, remainder iron including melting-related
impurities.
De bimetaal zaagband die uit een steunband die van hoge microstructurele stabiliteit en moeheidssterkte bestaat, uit 0,25 tot 0,35% van koolstof, 0,3 tot 0,5% van silicium bestaat, 0,8 tot 1,5% van mangaan, 1,0 tot 2,0% van molybdeen, 1,5 tot 3,5% van chromium, 0,5 tot 1,5% van nikkel, 0,5 tot 2,5% van wolfram, 0,15 tot 0,30% van vanadium, 0,05 tot 0,10% van niobium, 0,05 tot 1,0% van koper, tot 0,2% van aluminium, tot 1% van kobalt, restijzer met inbegrip van op smelten betrekking hebbende onzuiverheden, en tanduiteinden maakte van een staal met hoge slijtageweerstand, bestaand uit 1,0 tot 2,0% van koolstof, 3 tot 6% van chromium, 1 aan th, comprising 0.25 to 0.35% of carbon, 0.3 to 0.5% of silicon, 0.8 to 1.5% of manganese, 1.0 to 2.0% of molybdenum, 1.5 to 3.5% of chromium, 0.5 to 1.5% of nickel, 0.5 to 2.5% of tungsten, 0.15 to 0.30% of vanadium, 0.05 to 0.10% of niobium, 0.05 to 1.0% of copper, up to 0.2% of aluminum, up to 1% of cobalt, remainder iron including melting-related impurities, and tooth tips made from a steel with high wear resistance, comprising 1.0 to 2.0% of carbon, 3 to 6% of chromium, 1 to 5% of vanadium, 3 to 10% of molybdenum, 4 to 10% of tungsten, 4 to 10% van kobalt, tot 1% van silicium, tot 1% van mangaan, tot 0,5% van niobium, tot 0,5% van stikstof, restijzer met inbegrip van op smelten betrekking hebbende onzuiverheden.