The instant invention is directed to a bonded product, such as a manifold,
for gas or liquid chromatographs, and a method for making the same. The
bonded product is made using the following steps: (i) contacting two or
more steel sheets; (ii) heating the contacted sheets to a temperature
substantially below the melting temperature of the sheets; (iii) applying
pressure to the contacted sheets; and (iv) cooling the contacted sheets.
No intermediate foreign material is used to bond the steel sheets, e.g.,
no welding material or TLP diffusion bonding plate is utilized.
Nonetheless, a strong, leak free bond is generated at temperatures as low
as 1700.degree. F. (926.6.degree. C.). The bond is molecular in nature, as
evidenced by grains that grow from one sheet to another across the
interface between the two sheets.
The instant вымысел направлен к bonded продукту, such as коллектор, для хроматографов газа или жидкости, и методу для делать эти же. Сделан bonded продукт использующ following шаги: (i) контактируя два или несколько стальных листов; (ii) нагрюющ контактированные листы к температуре существенн под плавя температурой листов; (iii) придавать давление к контактированным листам; и (iv) охлаждающ контактированные листы. Никакой промежуточный чужеродный материал не использован для того чтобы скрепить стальные листы, например, не использованы никакой материал заварки или диффузия TLP плита bonding. Тем не менее, сильная, скрепление утечки свободно произведена на температурах как низких как 1700.degree. F (C 926.6.degree.). Скрепление молекулярно по сути, как проявлено зернами которые растут от одного листа к другим через поверхность стыка между 2 листами.