A high-carbon steel wire rod with superior drawability which has the
chemical composition (in mass %) of C: 0.6-1.0%, Si: 0.1-1.5%, Mn:
0.3-0.9%, P: no more than 0.02%, S no more than 0.03%, N: no more than
0.005%, (optional Nb: 0.020-0.050% and V: 0.05-0.20%), with the remainder
being Fe and inevitable impurities, and the structure which is
characterized in that pearlite accounts for no less than 95 area % and
pearlite has an average nodule diameter (P .mu.m) no larger than 30 .mu.m
and an average lamella space (S nm) no smaller than 100 nm such that the
value of F calculated by the formula below is larger than zero
F=350.3/S+130.3/P-51.7.
Una barra de alambre de acero high-carbon con el drawability superior que tiene la composición química (en % totales) de C: 0.6-1.0%, silicio: 0.1-1.5%, manganeso: 0.3-0.9%, P: no más de 0.02%, S no más de 0.03%, N: no más de 0.005%, (NOTA opcional: 0.020-0.050% y V: 0.05-0.20%), con el resto siendo FE e impurezas inevitables, y la estructura que se caracteriza en que el pearlite considera ningún menos de 95 áreas % y pearlite tiene un diámetro medio del nódulo (mu.m de P) no más en gran parte el mu.m de 30 y una laminilla media espacian (S nm) no más pequeño que 100 nm tales que el valor de F calculado por el fórmula abajo es más grande que F=350.3/S+130.3/P-51.7 cero.