A sintered steel and a method for the manufacture thereof are described,
the sintered steel being made by a method comprising the steps of
providing a first pre-alloyed steel powder having a composition comprising
in weight %: C 0.5-2, Cr 3.5-6, (2 Mo+W) 12-22, V 0.5-5, Co 0-12, Mn
0.1-0.5, Si 0.1-0.6, Fe balance apart from incidental impurities;
providing a second pre-alloyed steel powder having a composition
comprising in weight %: C 0.3-0.7, Cr 3-5.5, Mo 1-2.5, V 0.3-1.5, W 0-2,
Mn 0.1-0.6, Si 0.8-1.2. Fe balance apart from incidental impurities;
mixing together from 2 to 50 weight % of the first pre-alloyed steel
powder with 98 to 50 weight % of the second pre-alloyed steel powder
optionally up to 60 weight % of an iron powder and with carbon powder such
that the final carbon content of the matrix of the sintered steel powder
is a maximum of 1.1 weight %1; compacting the mixture and sintering to
form the sintered steel.
Un acier aggloméré et une méthode pour la fabrication en sont décrits, l'acier aggloméré fait par une méthode comportant les étapes de fournir une première poudre en acier pré-alliée ayant une composition comporter dans le poids % : C 0.5-2, le Cr 3.5-6, (2 Mo+W) 12-22, V 0.5-5, Co 0-12, le manganèse 0.1-0.5, le silicium 0.1-0.6, équilibre de Fe indépendamment des impuretés fortuites ; fournir un deuxième pré-a allié la poudre en acier ayant une composition comporter dans le poids % : C 0.3-0.7, le Cr 3-5.5, MOIS 1-2.5, V 0.3-1.5, W 0-2, le manganèse 0.1-0.6, le silicium 0.8-1.2. Équilibre de Fe indépendamment des impuretés fortuites ; le mélange ensemble de de 2 à 50 poids % du premier pré-a allié la poudre en acier avec 98 à 50 poids % de la deuxième poudre en acier pré-alliée sur option jusqu'à 60 poids % d'une poudre de fer et avec la poudre de carbone tels que la teneur finale en carbone de la matrice de la poudre en acier agglomérée est un maximum de 1.1 poids %1 ; compactage du mélange et agglomération pour former l'acier aggloméré.