A process for producing a carbon fiber sheet, which comprises allowing, as
necessary, an oxidized polyacrylonitrile fiber sheet to contain 0.2 to 5%
by mass of a resin, then subjecting the resin-containing oxidized
polyacrylonitrile fiber sheet to a compression treatment in the thickness
direction under the conditions of 150 to 300.degree. C. and 5 to 100 MPa
(10 to 100 MPa when no resin treatment is made) to obtain a compressed,
oxidized fiber sheet having a bulk density of 0.40 to 0.80 g/cm.sup.3 and
a compression ratio of 40 to 75%, and thereafter subjecting the
compressed, oxidized fiber sheet to a carbonizing treatment, which carbon
fiber sheet has a thickness of 0.15 to 1.0 mm, a bulk density of 0.15 to
0.45 g/cm.sup.3, a carbon fiber content of 95% by mass or more, a
compression deformation ratio of 10 to 35%, an electric resistance of 6
m.OMEGA. or less and a feeling of 5 to 70 g.
Un procédé pour produire une feuille de fibre de carbone, qui comporte laisser, selon les besoins, une feuille polyacrylonitrile oxydée de fibre pour contenir 0.2 à 5% par la masse d'une résine, soumettant alors résine-contenir a oxydé la feuille polyacrylonitrile de fibre à un traitement de compression dans la direction d'épaisseur dans les conditions de 150 à 300.degree. C. et 5 à 100 MPa (10 à 100 MPa quand aucun traitement de résine n'est fait) pour obtenir une feuille comprimée et oxydée de fibre ayant une densité en bloc de 0.40 à 0.80 g/cm.sup.3 et d'un rapport de compression de 40 à 75%, et soumettant ensuite la feuille comprimée et oxydée de fibre à un traitement de carbonisation, que la feuille de fibre de carbone a une épaisseur de 0.15 à 1.0 millimètre, d'une densité en bloc de 0.15 à 0.45 g/cm.sup.3, d'une teneur en fibre de carbone de 95% par la masse ou de plus, un rapport de déformation de compression de 10 à 35%, une résistance électrique de 6 m.Oméga. ou moins et un sentiment de 5 à 70 g.