A hydrocarbon resin is prepared by (1) thermally polymerizing a mixture
consisting essentially of (a) about 5% to 25% by weight styrene or
aliphatic or aromatic substituted styrene, and (b) about 95% to 75% by
weight based on total monomer content of a cyclic diolefin component
comprising at least about 50% by weight dicyclopentadiene. A method of
producing an aromatic-modified resin having a Mz of less than 2000 through
the addition of about 5% to 25% by weight styrene in combination with
about 95% to about 75% DCPD monomer at a rate to consume styrene monomer
at a the rate at which it is added. Hydrogenation of this resin produces
light colored, thermally stable products that are useful as tackifiers in
adhesives.
Una resina dell'idrocarburo è preparata (1) termicamente polimerizzando una miscela che è costituita essenzialmente da (a) circa 5% - 25% di peso stirolo o stirolo sostituito alifatico o aromatico e (b) circa 95% - 75% di peso basato sul contenuto totale del monomero di un componente ciclico della glicolefina che contiene almeno circa 50% di peso dicyclopentadiene. Un metodo di produrre una resina aromatico-modificata che ha un Mz più meno di di 2000 attraverso l'aggiunta di circa 5% - 25% di peso stirolo congiuntamente a circa 95% al monomero di circa 75% DCPD ad un tasso per consumare il monomero dello stirolo all'il tasso a cui è aggiunto. L'idrogenazione di questa resina produce la luce colorata, termicamente prodotti stabili che sono utili come tackifiers in adesivi.