Provided is a carbon material having a superior reversibility in lithium
intercalation-deintercalation reaction, and a non-aqueous secondary
battery using the carbon material as an active material for a negative
electrode, which has a high energy density and an excellent rapid charging
and discharging characteristics. Graphite powder having a maximum particle
diameter of less than 100 .mu.m and an existing reaction of rhombohedral
structure in the crystalline structure of less than 20% is used as an
active material for the negative electrode of the non-aqueous secondary
battery. The graphite powder can be obtained by pulverizing raw graphite
with a jet mill, and subsequently treating the powder at a temperature
equal to or higher than 900.degree.C.
Op voorwaarde dat een koolstofmateriaal een superieure omkeerbaarheid in de reactie van lithium intercalation-deintercalation is hebben, en een niet-waterachtige secundaire batterij die het koolstofmateriaal gebruiken als actief materiaal voor een negatieve elektrode, die een hoge energiedichtheid en het uitstekende snelle laden en het lossen kenmerken heeft. Het grafiet poeder dat een maximumdeeltjesdiameter van wordt minder dan mu.m 100 en een bestaande reactie van rhombohedral structuur in de kristallijne structuur van minder heeft dan 20% gebruikt als actief materiaal voor de negatieve elektrode van de niet-waterachtige secundaire batterij. Het grafietpoeder kan worden verkregen door ruw grafiet met een straalmolen te verpulveren, en later het poeder bij een temperatuur gelijk aan of te behandelen hoger dan 900.degree.C.