A niobium sintered body which is prepared in such a manner that a niobium
powder is sintered at a temperature of 500.degree. C. to 2000.degree. C.
and allowed to stand at a maximum sintering temperature for 60 minutes to
150 minutes in the course of sintering. The niobium sintered body of the
present invention is characterized in that a product (CV) of a capacitance
(C) per unit mass and a forming voltage (V) is 90,000 .mu.F.multidot.V/g
or more, and a value obtained by dividing a product of a mean particle
diameter (D.sub.50) of a primary particle of said niobium powder and a
leakage current (LC) by said CV is 5.times.10.sup.-4 .mu.m.multidot..mu.A
(.mu.F.multidot.V) or less. And there can be provided a well-balanced
capacitor with respect to a preferably low leakage current value
regardless of the large capacitance, that is, a highly reliable
capacitance.
Um niobium sintered o corpo que é preparado em tal maneira que um pó do niobium sintered em uma temperatura de 500.degree. C. a 2000.degree. C. e reservado para estar em uma temperatura máxima sintering para 60 minutos a 150 minutos no curso de sintering. O corpo sintered niobium da invenção atual é caracterizado que um produto (CV) de uma capacidade (C) por a massa da unidade e uma tensão dando forma (V) é o mu.F.multidot.V/g 90.000 ou o mais, e um valor obtido dividindo um produto de um diâmetro médio da partícula (D.sub.50) de uma partícula preliminar do pó dito do niobium e de uma corrente do escapamento (LC) por CV dito é o mu.m.multidot..mu.A 5.times.10.sup.-4 (mu.F.multidot.V) ou o menos. E lá pode ser fornecido um capacitor bem-equilibrado com o respeito a um valor atual do escapamento preferivelmente baixo não obstante a capacidade grande, isto é, uma capacidade altamente de confiança.