The present invention refers to a microporous material formed by oxygen,
silicon, germanium, aluminum, boron, gallium, zirconium and/or titanium in
its composition, called TIQ-6, to its catalytic applications in oxidation
reactions, and to a method of the TIQ-6 material's preparation based on
the synthesis of a gel with a titanium and/or zirconium content, its
hydrothermal treatment under controlled conditions, and the treatment of
the resulting laminar material with a solution of an organic compound
containing a proton accepting group. This swollen material is subjected to
a specific treatment to obtain a high external area delaminated solid. A
material, METIQ-6, similar to the TIQ-6 material, but also having organic
groups anchored on its surface incorporated by a post-synthesis process
onto the TIQ-6 material is also claimed.
La présente invention se rapporte à un matériel microporeux constitué par l'oxygène, silicium, germanium, aluminium, bore, gallium, zirconium et/ou titane en sa composition, appelée TIQ-6, à ses applications catalytiques dans des réactions d'oxydation, et à une méthode de la préparation du matériel TIQ-6 basée sur la synthèse d'un gel avec un contenu de titane et/ou de zirconium, son traitement hydrothermique dans des conditions commandées, et le traitement du matériel laminaire résultant avec une solution d'un composé organique contenant un proton acceptant le groupe. Ce matériel gonflé est soumis à un traitement spécifique pour obtenir un secteur externe élevé delaminated le solide. Un matériel, METIQ-6, semblable au matériel TIQ-6, mais à avoir également les groupes organiques ancrés sur sa surface incorporée par un processus de poteau-synthèse sur le matériel TIQ-6 est également réclamé.