The invention provides a low density paperboard material for use in
producing an insulated container, and is especially well-suited for making
cups. The paperboard material comprises a paperboard web including wood
fibers and expanded microspheres, and has a relatively low density ranging
from about 6 to about 10 lb/3MSF/mil, a relatively high caliper ranging
from about 24 to about 35 mil, and an internal bond strength of at least
about 80.times.10.sup.-3 ft-lb.sub.f preferably at least
100.times.10.sup.-3 ft-lb.sub.f. For applications such as cups the
material is also coated on one or both sides with a barrier coating,
preferably low density polyethylene, to limit liquid penetration into the
web. The low density paperboard material of the invention is convertible
for manufacture of containers, particularly cups, and the surface of the
low density board may have a Sheffield smoothness of 300 SU or greater.
Вымысел обеспечивает материал paperboard низкой плотности для пользы в производить изолированный контейнер, и специально well-suited для делать чашки. Материал paperboard состоит из стержня paperboard включая деревянные волокна и расширенные микросферы, и имеет относительно низкую плотность заколебаться от около 6 до около 10 lb/3MSF/mil, относительно высокого крумциркуля колебаясь от около 24 к mil около 35, и внутренне bond прочности по крайней мере около 80.times.10.sup.-3 ft-lb.sub.f предпочтительн по крайней мере 100.times.10.sup.-3 ft-lb.sub.f. Для применений such as чашки материал также покрын на одной или обеих сторонах с покрытием барьера, полиэтиленом предпочтительн низкой плотности, для того чтобы ограничивать жидкостное проникание в стержень. Материал paperboard низкой плотности вымысла обратим для изготовления контейнеров, определенно чашек, и поверхность доски низкой плотности может иметь гладкость sheffield 300 SU или больш.