A method for preparing a composite alkaline solid polymer electrolyte from
polyvinyl alcohol (PVA) polymer, potassium hydroxide and water. The
polymer electrolyte is reinforced with glass-fiber cloth to increase a
mechanical strength, thermal stability and electrochemical stability. A
glass fiber cloth matrix provides a stable interface between a cathode and
an anode to reduce a short circuit problem when the battery discharges at
high rate. The processes for polymer electrolyte are controlled by
molecular weight of PVA polymer, the sequence of feeding in reactants, the
weight proportions of reactants, the reaction time, the reaction
temperature, and the drying conditions, i.e., under the specified
conditions of relative humidity (RH), temperature and drying time. The
resulting electrolyte exhibits ionic conductivity of 0.15 S/cm or better
at room temperature and has high mechanical intensity and good
electrochemical stability.
Μια μέθοδος για έναν σύνθετο αλκαλικό στερεό πολυμερή ηλεκτρολύτη από το πολυμερές σώμα πολυβινυλικού οινοπνεύματος (PVA), το υδροξείδιο καλίου και το ύδωρ. Ο πολυμερής ηλεκτρολύτης ενισχύεται με το ύφασμα γυαλί-ινών για να αυξήσει μια μηχανική δύναμη, μια θερμική σταθερότητα και μια ηλεκτροχημική σταθερότητα. Μια μήτρα υφασμάτων ινών γυαλιού παρέχει μια σταθερή διεπαφή μεταξύ μιας καθόδου και μιας ανόδου για να περιορίσει ένα σύντομο πρόβλημα κυκλωμάτων όταν απαλλάσσει η μπαταρία στο υψηλό ποσοστό. Οι διαδικασίες για τον πολυμερή ηλεκτρολύτη ελέγχονται από το μοριακό βάρος PVA του πολυμερούς σώματος, η ακολουθία σίτισης στα αντιδραστήρια, τα ποσοστά βάρους των αντιδραστηρίων, ο χρόνος αντίδρασης, η θερμοκρασία αντίδρασης, και οι όροι ξήρανσης, δηλ., κάτω από τους διευκρινισμένους όρους της σχετικής υγρασίας (RH), τη θερμοκρασία και το χρόνο ξήρανσης. Ο προκύπτων ηλεκτρολύτης εκθέτει την ιοντική αγωγιμότητα 0,15 S/cm ή καλύτερος στη θερμοκρασία δωματίου και έχει την υψηλή μηχανική ένταση και την καλή ηλεκτροχημική σταθερότητα.