A low melting point metal material is made to a thixotropic state in which
liquid phases and solid phases coexists. In the thixotropic state of the
low melting point metal material, a carbon nano material is kneaded with
the low melting point metal material and forms a composite material. Thus
obtained composite material is supplied to a metal molding machine and
injected into a mold in a thixotropic state or a completely molten state
of the metal so that the composite material fills the mold, thereby the
composite material is molded to a composite metal product. With the above
process, it is possible to injection mold the composite metal product to
which the characteristics of the carbon nano material are applied.
Низкий материал металла точки плавления сделан к тиксотропному положению в жидкостные участки и твердые участки сосуществуют. В тиксотропном положении низкого материала металла точки плавления, материал nano углерода замешан с низким материалом металла точки плавления и формирует составной материал. Таким образом полученный составной материал поставлен к машине прессформы металла и после того как я впрыснут в прессформу в тиксотропном положении или вполне жидком положении металла так, что составной материал заполнит прессформу, таким образом составной материал отлит в форму к составному продукту металла. С вышеуказанным процессом, по возможности к прессформе впрыски составной продукт металла к которому приложены характеристики материала nano углерода.