An olefin-based resin composition contains (a) 39-94 parts by weight of a
propylene homopolymer or propylene-ethylene copolymer of at least 50 wt. %
propylene content, having a melt-flow rate of 0.1-5 g/10 min, (b) 1-20
parts by weight of a polypropylene modified with 0.1-10% by weight of an
acid anhydride, (c) 5-60 parts by weight of a styrene-based polymeric
elastomer modified with 0.1-10% by weight of an acid anhydride, the total
of components (a), (b) and (c) being 100 parts by weight, and (d) 30-200
parts by weight of a metal hydroxide. This halogen-free resin composition
has a good balance of properties such as wear resistance, flame
resistance, tensile properties and flexibility, which are required for the
covering material of an electrical wire for an automobile.
Een op olefin-gebaseerde harssamenstelling bevat (a) 39-94 delen bij het gewicht van een propyleenhomopolymeer of een propyleen-ethyleen copolymeer van de inhoud van het minstens 50 % gew.propyleen, die een smelting-stroom tarief van 0,1-5 g/10 min heeft, (b) 1-20 delen bij het gewicht van een polypropyleen dat met 0,1-10% bij het gewicht van een zuur anhydride wordt gewijzigd, (c) 5-60 delen bij het gewicht van een op styreen-gebaseerd polymeer elastomeer dat met 0,1-10% bij het gewicht van een zuur anhydride wordt gewijzigd, het totaal van componenten (a), (b) en (c) dat 100 delen in gewicht, en (d) 30-200 delen bij het gewicht van een metaalhydroxyde zijn. Deze halogeen-vrije harssamenstelling heeft een goed saldo van eigenschappen zoals slijtageweerstand, vlamweerstand, trekeigenschappen en flexibiliteit, die voor het behandelende materiaal van een elektrodraad voor een auto worden vereist.