A composition exhibiting reverse thermal gellation properties comprises a
block polymer having the structure:
{[A.sub.n (BCB)A.sub.n ]}.sub.m
wherein A is a polyester unit, B is a poly(ethylene oxide) unit, C is a
poly(propylene oxide) unit, E is a chain extender unit, n=0-20, and m is
greater than 2. The ethylene oxide:propylene oxide ratio ranges from about
0.2:1 to about 40:1. The composition has a final viscosity at a final
temperature of more than twice the initial viscosity at an initial
temperature wherein the final temperature is at least 10.degree. C. higher
than the initial temperature. The composition is combined with either a
cellular material for tissue engineering, a cellular material for
effecting repair or healing in a patient, or a bioactive agent.
Una composición que exhibe características termales reversas del gellation abarca un polímero del bloque que tiene la estructura: {la unidad [ de A.sub.n (BCB)A.sub.n ]}.sub.m en donde A es una unidad del poliester, B es un óxido del poly(ethylene), C es un óxido del poly(propylene) la unidad, E es una unidad de cadena del suplemento, n=0-20, y m es mayor de 2. El cociente del óxido del etileno oxide:propylene se extiende de cerca de 0.2:1 a cerca de 40:1. La composición tiene una viscosidad final en una temperatura final más de dos veces de la viscosidad inicial en una temperatura inicial en donde la temperatura final es por lo menos 10.degree. C. más arriba que la temperatura inicial. La composición se combina con un material celular para la ingeniería del tejido fino, un material celular para efectuar la reparación o curativo en un paciente, o un agente bioactive.