The present invention relates to an improved high-performance permeable
concrete obtained by spreading and compacting a mixture which comprises
1,500-1,850 kg/m.sup.3 of aggregates; 320-400 kg/m.sup.3 of Portland
cement; 28-35% of the cement (90-140 kg/m.sup.3) of water; 2-5% of the
cement (6-20 kg/m.sup.3) of a pigment; and 3-10% of the cement (10-40
kg/m.sup.3) of charcoal dust, 7-15% of the cement (22-60 kg/m.sup.3) being
substituted for particulates of blast furnace slag, and having the
compressive strength of 120-300 kgf/cm.sup.2 and the permeability
coefficient of 2.times.10.sup.-2 cm/sec or more. The permeable concrete
according to the present invention is environmental friendly and has
excellent strength and permeability.
La actual invención se relaciona con un concreto permeable de alto rendimiento mejorado obtenido separando y condensando una mezcla que abarque 1.500-1.850 kg/m.sup.3 de agregados; 320-400 kg/m.sup.3 del cemento de Portland; 28-35% del cemento (90-140 kg/m.sup.3) del agua; 2-5% del cemento (6-20 kg/m.sup.3) de un pigmento; y 3-10% del cemento (10-40 kg/m.sup.3) del polvo de carbón de leña, 7-15% del cemento (22-60 kg/m.sup.3) que es substituido para los particulates de la escoria del alto horno alto, y teniendo la fuerza compresiva de 120-300 kgf/cm.sup.2 y el coeficiente de la permeabilidad de 2.times.10.sup.-2 cm/sec o más. El concreto permeable según la actual invención es amistoso ambiental y tiene fuerza y permeabilidad excelentes.