A metal foil for a current collector of a secondary battery formed by
electrodeposition and has a thickness (T) of 8 to 40 .mu.m, the metal foil
satisfying the following formulae:
4.9.times.10.sup.8.ltoreq.T.times.S.times.Y.ltoreq.31.times.10.sup.8
4.5.ltoreq..epsilon.-(0.0005.times.T.sup.2).ltoreq.15
where S is a breaking strength (MPa), .epsilon. is a tensile elongation (%)
and Y is a Young's modulus (MPa).
This foil is preferably a nickel foil and is manufactured by softening or
annealing the metal foil obtained by electrodeposition. Thereby, a metal
foil for a negative electrode of a secondary battery is obtained with an
excellent capability of supporting the active material and large electric
conductivity.
Eine Metallfolie für einen Stromabnehmer einer Sekundärbatterie bildete sich durch galvanischen Niederschlag und hat eine Stärke (T) von 8 bis 40 mu.m, die Metallfolie, welche die folgenden Formeln erfüllt: 4.9.times.10.sup.8.ltoreq.T.times.S.times.Y.ltoreq.31.times.10.sup.8 4.5.ltoreq..epsilon.-(0.0005.times.T.sup.2).ltoreq.15 wo S eine Bruchfestigkeit (MPa) ist, epsilon. ist eine dehnbare Verlängerung (%) und Y ist ein der Jugend Modul (MPa). Diese Folie ist vorzugsweise eine Nickelfolie und wird hergestellt, indem sie die Metallfolie erweicht oder tempert, die durch galvanischen Niederschlag erreicht wird. Dadurch wird eine Metallfolie für eine negative Elektrode einer Sekundärbatterie mit einer ausgezeichneten Fähigkeit des Stützens des aktiven Materials und der großen elektrischen Leitfähigkeit erreicht.