An alkali-free glass consists essentially of, in mass percent, 58-70%
SiO.sub.2, 10-19% Al.sub.2 O.sub.3, 6.5-15% B.sub.2 O.sub.3, 0-2% MgO,
3-12% CaO, 0.1-5% BaO, 0-4% SrO, 0.1-6% BaO+SrO, 0-5% ZnO, 5-15%
MgO+CaO+BaO+SrO+ZnO, 0-5% ZrO.sub.2, 0-5% TiO.sub.2, and 0-5% P.sub.2
O.sub.5. The alkali-free glass contains substantially no alkali metal
oxide and has a density of 2.45g/cm.sup.3 or less, an average coefficient
of thermal expansion of 25.times.10.sup.-7 /.degree. C.-36.times.10.sup.-7
/.degree. C. within a temperature range between 30 and 380.degree. C., and
a strain point not lower than 640.degree. C.
Алкали-svobodno стекло состоит необходимо, в массовых процентах, 58-70% SiO.sub.2, 10-19% Al.sub.2 O.sub.3, 6.5-15% B.sub.2 O.sub.3, 0-2% mgO, 3-12% caO, 0.1-5% BaO, 0-4% SrO, 0.1-6% BaO+SrO, 0-5% ZnO, 5-15% MgO+CaO+BaO+SrO+ZnO, 0-5% ZrO.sub.2, 0-5% TiO.sub.2, и 0-5% P.sub.2 O.sub.5. Алкали-svobodno стекло содержит substantially no окись металла алкалиа и имеет плотность 2.45g/cm.sup.3 или, средний коэффициент термального расширения 25.times.10.sup.-7 /.degree. C.-36.times.10.sup.-7 /.degree. C внутри температурная амплитуда между 30 и 380.degree. C, и пункт напряжения более низкий чем 640.degree. Ч.