In the method of the present invention, xylylenediamine is produced by a
two-stage hydrogenation of a dicyanobenzene compound. In a first stage
(a), the hydrogenation is performed until a conversion of nitrile groups
reaches 90 mol % or higher and less than 99.9 mol %. In a second stage
(b), the hydrogenation is further continued at temperatures 10.degree. C.
or more higher than in the step (a) until the conversion of nitrile groups
reaches a level which is higher than that attained in the step (a) and
equal to 99.5 mol % or more. In the present invention, a highly pure
xylylenediamine containing a minimized amount of cyanobenzylamine is
efficiently produced in a simple manner without needing a specific
purification, and also without deteriorating the use efficiency of the
catalyst while reducing the amount of the dicyanobenzene compound
remaining not reacted and the generation of the intermediate
cyanobenzylamine.
No método da invenção atual, o xylylenediamine é produzido por um hydrogenation two-stage de um composto do dicyanobenzene. Em um primeiro estágio (a), o hydrogenation é executado até que uma conversão de grupos do nitrile alcance 90 mol de % ou mais altamente e menos de 99.9 mol de %. em um segundo estágio (b), o hydrogenation é continuado mais mais nas temperaturas 10.degree. C. ou mais altamente do que na etapa (a) até que a conversão do nitrile agrupar alcances um nível que seja mais elevado do que aquele alcançado na etapa (a) e no igual a 99.5 mol de % ou mais. Na invenção atual, um xylylenediamine altamente puro que contem uma quantidade minimizada de cyanobenzylamine é produzido eficientemente em uma maneira simples sem necessitar um purification específico, e também sem deteriorar a eficiência do uso do catalizador ao reduzir a quantidade do não reagido restante do composto do dicyanobenzene e a geração do cyanobenzylamine intermediário.